不锈钢丝网,stainless steel wire mesh
1)stainless steel wire mesh不锈钢丝网
1.The effect of preparation parameters on the structure and catalytic performance of Ce-Pt-Pd/SSWMstainless steel wire mesh catalyst制备参数对不锈钢丝网催化剂结构和性能的影响
英文短句/例句
1.Preparation and Performance of Ce-Pt-Pd/Stainless Steel Wire Meshes CatalystCe-Pt-Pd/不锈钢丝网催化剂的制备与催化性能
2.Pd-Y/Stainless Steel Wire Mesh Catalyst for Combustion of Volatile Organic CompoundsVOCs催化燃烧Pd-Y/不锈钢丝网催化剂的性能
3.The effect of preparation parameters on the structure and catalytic performance of Ce-Pt-Pd/SSWM stainless steel wire mesh catalyst制备参数对不锈钢丝网催化剂结构和性能的影响
4.Effects of Adding Cerium on the Structures and Properties of Supported Pd/Stainless Steel Catalyst with Porous Oxides Film铈的引入对负载钯阳极氧化膜不锈钢丝网催化剂结构和性能的影响
5.stainless steel wire wrapped scree不锈钢钢丝绕制筛管
6.Stainless steel wire ropesGB/T9944-1988不锈钢丝绳
7.Pore and Permeation of Composite of Stainless Steel Powders and Silkscreen不锈钢粉末与丝网复合的孔隙和透过性能
8.cloth wire of iron or steel whether or not stainless丝布,铁或钢（无论是否不锈钢）制
9.stainless steel net-cover of axial fan不锈钢轴流风机网罩
10.There were no significant differences of frictional resistance between 0.020 inch stainless steel round wire and 0.019× 0.025 inch stainless steel rectangular wire.0.020英寸不锈钢圆丝与0.019×0.025英寸不锈钢方丝之间无显著差异。
11.The center wire is usually of tungsten or stainless steel and is about 0.1 mm in diameter.中心丝通常是钨丝或不锈钢丝，直径约为0．1毫米。
12.At present, it"s widely used in the production of steel made furniture, stainless products, theft-proof door, kitchen fitting ad repair welding of wire lath.目前广泛用于钢制家具，不锈钢制品，防盗门生产，厨房设备及钢丝网片补焊等。
13.Development of duplex stainless steel flux-cored wire GDQA2205双相不锈钢药芯焊丝GDQA2205的研制
14.Stainless Steel/Stainless Steel Countersunk不锈钢/不锈钢 沉头型
15.Stainless Steel/Stainless Steel Standard不锈钢/不锈钢 标准型
16.Stainless Steel/Stainless Steel Dome Head不锈钢/不锈钢 圆头型
17.Stainless Steel/Steel Dome Head不锈钢/钢 圆头型
18.Stainless Steel/Steel Countersunk不锈钢/钢 沉头型
相关短句/例句
stainless wire mesh不锈钢网丝
1.Analysis present that pitting corrosion and stress corrosion are the mainly reasons for the crack ofstainless wire mesh.结果表明,不锈钢网丝的点腐蚀和应力腐蚀是造成网丝断裂的根本原因,由于不锈钢网丝的断裂,导致波纹管失去丝网的保护和轴向伸长的约束,波纹管在内压作用下冲破丝网的约束,进而产生过度弯曲变形,在波纹管与短接管焊接的薄弱处因过载而发生断裂。
3)Hstainless steel mesh substrate不锈钢丝网基底
4)stainless steel wire不锈钢丝
1.Technology of removing deformation magnetic property of metastable austenitestainless steel wire消除亚稳定奥氏体不锈钢丝形变磁性的技术
2.The microstructure and mechanical properties ofstainless steel wires used for metal rubber were studied by means of optical microscopy,SEM,and X-ray diffraction.15mm的Cr-N i-Mn系不锈钢丝的微组织结构和力学性能的变化规律。
3.There is a coat of oxide on the surface of the heat treatedstainless steel wire,which is difficult to be cleaned.不锈钢丝热处理后表面形成一层难以清除的氧化皮 ,4 80℃高温碱煮和 85℃高锰酸钾碱液的清洗对比试验和应用显示高锰酸钾碱洗工艺可行 ,但要求KMnO4 和NaOH浓度大于 80g L ,溶液温度高于 80℃ ,清洗时间5～ 10min ,比碱煮少 5min ;高锰酸钾碱液清洗效果好 ,不锈钢丝表面无黑色胶状物 ,而且不会产生过腐蚀 ,每吨不锈钢丝可节省电能 1875kW·h ,劳动环境也有很大改
5)stainless steel mesh不锈钢网
1.The LaNiO3 film was synthesized on thestainless steel mesh(SSM).在不锈钢网(SSM)表面上合成了LaNiO3催化剂前驱体薄膜。
6)stainless steel powders and silkscreen不锈钢粉末与丝网
1.Pore and permeation of composite ofstainless steel powders and silkscreen were researched, which depended on the particle size, especially that of the last layer.不锈钢粉末与丝网复合的孔隙和透过性能研究表明,料浆粒度显著影响孔隙和透过性能,末级料浆粒度起决定性作用;二次双向涂覆时,相同料浆粒度料浆形成外细内粗的三明治结构,不同粒度料浆形成由粗到细的梯度结构;复合多孔材料具有均匀的孔径分布和高透过率。
延伸阅读
钢丝网钢丝网steel wire meshgongSIW0ng钢丝网(steel wire mesh)由钢丝编织或焊接而成的具有网孔的钢丝制品。钢丝网广泛应用于冶金、矿山、国防及工农业生产等各个部门，做筛选、防护、隔离、建筑材料之用。分类和规格丝网根据使用场所和使用性能的不同有几十个品种。按有无镀层分，有光面钢丝网、镀锌钢丝网、涂塑钢丝网;按材料性质分，有普通低碳钢丝网、耐热合金钢丝网、耐蚀不锈钢丝网;按加工方式分，有编织钢丝网和焊接钢丝网。钢丝网的规格型号以钢丝、网孔和网幅表示。网丝用线号或英寸、毫米表示，网孔用孔径、网目或网号表示。网目指1英寸长度内网孔的个数，英美等国常以网目表示网孔大小，中国以孔径或网目表示之，前苏联以网号表示。网号指网孔的公称尺寸，如1.0号网指正方形孔每边长1.omm。品种及工艺常见的钢丝网品种及网孔形状如图所示，有方形孔、菱形孔、六角孔、梯形孔等数种。方形孔有波形方孔(眼)网、镀锌电焊网、平纹网几种。波形方孔网又称拨花网或轧花网，如图a所示，网的经线和纬线经过预先弯曲成波状，再行织造，网孔结合牢固，网孔方正，抗拉力好，耐磨性强，不易变形。镀锌电焊方孔网，如图b所示，结构坚固，整体性强，点焊后再电镀，具有很好的防蚀能力。菱形网亦称斜方孔网，如图‘所示，一般用低碳镀锌钢丝预先扭成扣状，然后编织。使用时网边须拉紧，否则网扣易松弛，影响网的整体性。六角网亦称拧花网、龟甲网，如图d所示。网孔为六角形，按加工工艺有先镀后编织和先编织后镀两种。图h所示是一种带加强筋的六角网，抗拉力比一般六角网大，布筋间隔根据用途而有所不同。梯形网如图e所示，网孔呈梯形，主要用于建材中作波瓦和保温墙的加强网。另一种矿筛网如图f所示，用于筛选矿石，网孔较粗，丝径为5.omm或6.otnm，单位网面工作压力达1一1.skPa。